Paul,
Although you have an interesting theory, I don't think many people would consider cast iron manifolds to be wear items!
There has to be some sort of stress that's causing these to crack. Extreme heat from running lean could be a contributing factor -- I saw my manifolds glow orange one time when I had my idle mixture set too lean
Brian